Title |
Development and Property Analysis of Segregation-Reducing Type Flowing Concrete Using the Viscosity Agent
|
|
Keywords |
segregation-reducing type flowing concrete; viscosity agent; combined superplasticizer |
|
Abstract |
When superplasticizer is added to manufacture flowing concrete, the base concrete usually needs the adjustment to assure the sufficient fines contained to obtain flowable consistency without excessive bleeding or segregation. However, this may not only increase the cost, but also cause inconvenience in producing the base concrete. In this paper, the experiments are performed on normal base concrete to achieve a segregation-reducing flowing concrete by adding superplasticizer mixed with viscosity agents and AE admixtures. Three kinds of superplasticizer and two kinds of viscosity agent are selected. According to the results, with regard to the performance and cost of the admixtures, melamine type superplasticizer combined with the PEO viscosity agent and AE admixtures at the ratio 1:0.28:0.001 can acquire good quality and reduce the cost in producing the flowing concrete. With proper addition of combined superplasticizer, even though water to cement ratios of the base concrete are different, the segregation-reducing flowing concrete could be also achieved without reproportioning of the base concrete. However, it would be more desirable if the superplasticizer could be adjusted, before it is put into the practical use in order not to cause some other problems, such as rapid rate of slump loss and retarding of setting time.
|