Title |
An Experimental Study on the Properties of High Flowing Concrete according to Water/Binder Ratio(W/B)
|
|
Keywords |
고유동콘크리트; 물결합재비; 단위수량; 충전성; 재료분리저항성; high-flowing concrete; water/binder ratio(W/B); water content; compactibility; non-segregation ability |
|
Abstract |
Recently, in many laboratories and institutes it is being studied on the high flowing concrete widely, which has high fluidity, non-segregation ability and fillingability, and sometimes being applied to the construction field actually. And the fluidity properties of high flowing concrete are influenced according to the several factors ; binder content, water/binder ratio and water content etc. This is an experimental study to compare and analyze the effect of water/binder ratio and water content on the properties of high flowing concrete. For this purpose, the mix proportion of high flowing concrete according to water/binder ratio(W/B : 0.30, 0.35, 0.40, 0.45) and water content (W : 155, 165, 175, 185 kg/㎥) was selected. And then slump-flow, V-lot, L-passing test in fresh concrete, and compressive strength, freezing and thawing test in hardened concrete were peformed. According to test results, it was found that the viscosity of all those high flowing concrete with the water content 175 kg/㎥ was satisfied with 50 cm pass time of slump flow prescribed by Japanese Architectural Standard Specification (JASS 5) - from 3 to 8 seconds. And non-segregation ability of concrete with W/B 0.35 was better than the other mix proportions. Especially, the compressive strength after curing 24 hours(1 day) of all high flowing concrete was higher than that prescribed by JASS 5(50 kgf/㎠).
|