Development of Self Waterproofing Admixture for Concrete Using Inorganic Admixture
|
|
Keywords |
무기질 혼화재; 흡수성; 투수성; 구체방수재; inorganic admixture; absorption; permeability; self waterproofing admixture |
|
Abstract |
The watertight property of concrete was examined, that is affected by the sort of self waterproofing admixture and the change of the addition ratio of admixture. Various self waterproofing admixtures were made by changing the mixing ratio of silica fume, zinc stearate and silica sand. The result showed as follows. As the adding ratio of self waterproofing admixture increases, the fluidity is increased and the setting time is delayed. While compressive strength of concrete with self waterproofing admixture A which is currently using is increased until the adding ratio of self waterproofing admixture reached 18kg/㎥ and decreased over 24 kg/㎥, that with self waterproofing admixture B, C and D which are developed are higher than that of A. Absorption is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Especially, when self waterproofing admixture has a lot of zinc stearate, absorption is decreased manifestly. The property of permeability is similar to that of absorption; permeability is decreased as the adding ratio of self waterproofing admixture and the increasing of age in concrete. Consequently, when the ratio of silica fume, zinc stearate and silica sand in self waterproofing admixture is 1 : 2 : 1 and addition ratio of self waterproofing admixture is 6kg/㎥, the high quality concrete is obtained comparing to the concrete with existent self waterproofing admixture.
|