Strength Development and Permeability of Latex-Modified Concrete with Rapid-Setting Cement
|
|
Keywords |
초속경 라텍스 개질 콘크리트; 소포제; 라텍스; rapid-setting cement latex modified concrete(RSLMC); antifoam agent; latex |
|
Abstract |
The purpose of this research was to develop a rapid setting cement latex modified concrete (RSLMC) for bridge deck repairing and overlaying. The main experimental variables were latex contents, antifoamer contents and water-cement ratioes. The workability, strength development and permeability were measured as responses. The results showed that latex content increased the slump and reduced the unit water required for same workability. The air contents were measured as 8.0∼9.0％ and 2.0∼3.0％ without antifoamer and with 1.6∼3.2％ of antifoamer, respectively. This resulted in the increment of compressive strength development by 10∼20 ％. The flexural strength of RSLMC increased greatly as the latex content increased, but not in compressive strength. The compressive strength and flexural strength developed enough for opening the overlayed RSLMC to the traffic after 3 hours of RSLMC placement. The permeability of RSLMC was evaluated as negligible due to its very low charge passed. Thus, RSLMC could be used at repairing or overlaying the concrete bridge deck at fast-track job sites.
|