Damage of Overlaid Concrete Structures Subjected to Humidity Changes in the Atmosphere
|
|
Keywords |
보수체; 습도 변화; 비선형 응력-변형률 곡선; 변형률 연화특성; 경계면의 들뜸 현상; overlaid concrete structures; humidity changes; non linear stress-strain relationship; strain-softening; peel-off |
|
Abstract |
The failure phenomenon of overlaid concrete structures, such as surface crack, and peel-off failure, shear bond failure in the end contact zone, was investigated due to humidity changes. To investigate this failure phenomenon, the surface tensile stress, and the shear stress, the vertical tensile stress in the contact zone were analysed using the non-linear stress-strain relationship of material such as strain-hardening- and strain-softening diagrams. Overlay thickness and overlay material were the main variables in the analyses. It is assumed that the initial surface humidity of overlaid concrete structures was 100％ r.H. With a atmospheric humidity of 55％ r.H. and two load cases for drying(LCI), curing and drying(LC2), the stress states of overlaid concrete structures were calculated. The result shows that only fictitious cracks occurred in the overlay surface of CM2O, ECM25, and no shear bond failure occurred in the contact zone without CM2O. The peel-off failure was proved to be the main cause of the damage in the overlaid concrete structures. Only for overlay thickness of 1cm occurred no peel-off failure in the case of drying after a long-term public use(LC1). In the case of curing and drying during overlay work(LC2) occurred the peel-off failure within 1.5days for all the overlaid concrete structures.
|