| Title |
Influence of Mineral Admixtures on the Diffusion Coefficient for Chloride Ion in Concrete |
| Keywords |
diffusion coefficient for chloride ion;cement type;mineral admixture;water-binder ratio;염소이온 확산계수;시멘트 종류;광물질 혼화재;물-결합재비 |
| Abstract |
The qualitative factors influencing the ingress of chloride ion into concrete are water-binder (W/B) ratio, cement type, age, chloride ion concentration of given environment, wet and dry conditions, etc. Thus, an objective of this experimental research is to investigate the effects of cement types and environmental conditions on the chloride ion diffusion characteristics in concrete through the chloride ion diffusion test. For this purpose, the diffusion coefficients for chloride ion in concrete with three types of cement such as ordinary portland cement (OPC), binary blended cement (BBC), and ternary blended cement (TBC), were measured for the concrete specimens with W/B ratios of 32%, 38%, and 43%, respectively. The diffusion coefficients for chloride ion were also measured for the concrete specimens with W/B ratio of 43%, which were subjected to standard curing and field exposure conditions. It was observed from the test results that the resistance against chloride ion penetration increased with decreasing W/B ratio and those of BBC and TBC concretes were greater than that of OPC concrete. Therefore, it was revealed that the use of these cements containing mineral admixtures is required to extend the service life of RC structures exposed to chloride environment. On the other hand, it was noted that the resistance against chloride ion penetration of field exposure test specimens was slightly lower than that of standard curing test specimens due to the penetration of chloride ion under the irregular ambient temperature, splash of wave, and cycle of wet and dry. |