Effect of Curing Solution and Pre-Rust Process on Rebar Corrosion in the Cement Composite
|
|
Authors |
두여준(Rujun Du) ; 장인동(Indong Jang) ; 이혜린(Hyerin Lee) ; 이종구(Chongku Yi) |
|
DOI |
https://doi.org/10.11112/jksmi.2022.26.2.1 |
|
Keywords |
철근 부식 속도; 양생환경; 사전부식철근; 분극 저항 Corrosion rate; Curing solution; Pre-rusted rebars; Electrochemical polarization |
|
Abstract |
The corrosion of reinforcement is the main reason for the performance degradation of concrete structures. The pre-rusted parts of rebar in concrete structures are vulnerable to the corrosion, especially if the structure is exposed to wet or chlorinated environments. In this study, effects of different curing solution on corrosion behavior of the pre-rusted rebars in the cement composites were investigated. HCl(3%) and CaCl2(10%) solution were utilized to accelerate the pre-rust of the rebar, and each pre-rust condition rebar including reference (RE) were placed in mortar cylinder. Three kinds of samples then were cured in CaCl2 (3%) solution and tap water respectively for 120 days. Electrochemical polarization and half-cell potential measurement were used to monitor the influence of curing water on the corrosion behavior of pre-rusted steel bar in cement composite. The surface morphology and composition of corroded steel bar were analyzed by scanning electron microscope and energy dispersive X-ray diffraction. The results show that the corrosion rates of pre-rusted samples in both curing water are higher than that of non-pre-rusted samples. The corrosion rates of RE, CaCl2 and HCl pre-rusted samples in salt water were 8.14 ,4.48, 13.81 times higher than those in tap water respectively, on the 120th day.
|