| Title |
Development of Extra High Voltage(400kN) Porcelain Insulator for Transmission Lines |
| Keywords |
400kN suspension insulator ; Alumina porelain ; Puncture test ; Electro-mechanical faiing load ; termal-mechanical load cycle test |
| Abstract |
This paper was the research of high voltage suspension insulator (400 [kN]) including pottery stone, feldspar, clay and alumina of 17 [wt%]. The slurry was fabricated after ball milling mixed raw materials. Green compacts were made by the extrusion of jiggering method and were sintered at 1300[°C] for 50 [min.] in the tunnel kiln. The sintered density was reached to 97% of theoretical density, and the bending strength was 1658 [k g_{f}/ textrm cm^2] and hardness and fracture toughness which was measured by ICL( indentation crack length ) method were 1658 (kgf/ textrm cm^2) and 27.5 [Gpa], respectively. In measurement of tana and insulation break voltage of 400 (kN) porcelain, tanΔ took some numerical value between 17×10_{-3} and 61×10_{-3} and insulation break voltage value was 19.9 pm1.4 [㎸/mm]. The test was performed to research whether the shape of pin affect a overvoltage break load or not As a consequence, when a pin was designed a pin diameter 51 [mm] with the bottom form of two-step constructed with straight in the suspension insulator, Insulator showed overvoltage break load 52 [ton] of the highest value and reflected a fine characteristic in aged deterioration test which is one of the accelerated aging test. Also it could be confirmed a fine characteristic through performing the test that electrical property of insulator was established correctly in accordance with IEC 60383-1 standards.s. |